產(chǎn)品詳情
| PA66 71G33L 美國杜邦公司 物性數(shù)據(jù) |
| 暫無此原料描述部分┄ |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | 24小時浸漬(23℃) | ASTM D-570 | 0.5 | % |
| 吸水率 | 飽和(23℃) | ASTM D-570 | 4.6 | % | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.35 | --- |
| 機械性能 | 洛氏硬度M | DAM | ASTM D-785 | M96 | --- |
| 洛氏硬度M | 50%RH | ASTM D-785 | M90 | --- | |
| 洛氏硬度R | DAM | ASTM D-785 | R122 | --- | |
| 洛氏硬度R | 50%RH | ASTM D-785 | R118 | --- | |
| 泰伯磨耗量 | 50%RH | --- | 36 | cycles | |
| 拉伸強度 | 23℃,DAM | ASTM D-638 | 151.6 | MPa | |
| 拉伸強度 | 23℃,50%RH | ASTM D-638 | 110.3 | MPa | |
| 斷裂伸長率 | 23℃,DAM | ASTM D-638 | 3 | % | |
| 斷裂伸長率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
| 擠剪強度 | 23℃,DAM | ASTM D-732 | 72 | MPa | |
| 撓曲模量 | 23℃,DAM | ASTM D-790 | 6895 | MPa | |
| 撓曲模量 | 23℃,50%RH | ASTM D-790 | 5516 | MPa | |
| 撓曲強度 | 23℃,DAM | ASTM D-790 | 228 | MPa | |
| 埃佐沖擊強度 | 23℃,DAM | ASTM D-256 | 128 | j/m | |
| 埃佐沖擊強度 | 23℃,50%RH | ASTM D-256 | 128 | j/m | |
| 電氣性能 | 介電強度 | DAM | ASTM D-149 | 630 | volts/mil |
| 介電強度 | 100%RH | ASTM D-149 | 255 | volts/mil | |
| 體積電阻率 | 100%RH | ASTM D-257 | 109 | ohm-cm | |
| 損耗因數(shù) | DAM@106Hz赫 | ASTM D-150 | 0.02 | --- | |
| 體積電阻率 | DAM | ASTM D-257 | 1014 | ohm-cm | |
| 介電強度 | (分步法)DAM | ASTM D-149 | 510 | volts/mil | |
| 介電常數(shù) | DAM@103Hz赫 | ASTM D-150 | 4.2 | --- | |
| 介電常數(shù) | DAM@106Hz赫 | ASTM D-150 | 3.4 | --- | |
| 損耗因數(shù) | DAM@103Hz赫 | ASTM D-150 | 0.02 | --- | |
| 熱 性 能 | 熔點 | 50%RH | ASTM D-789 | 255 | ℃ |
| 線性熱膨脹系數(shù) | --- | ASTM D-696 | 1.8×10-5 | m/m/℃ | |
| 熔點 | DAM | ASTM D-789 | 255 | ℃ | |
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 246 | ℃ | |